| Designation |
Symbol |
Description |
| 交貨狀態(tài) |
代號(hào) |
說(shuō)明 |
| Cold finished (hard) |
BK（+C） |
Tubes do not undergo heat treatment following the final cold forming and, thus, have a rather high resistance to deformation |
| 冷加工（硬） |
最后冷加工之后不進(jìn)行熱處理， 從而管子只可能進(jìn)行很小的變形。 |
| Cold finished (Soft) |
BKW
（+LC） |
The final heat treatment is followed by cold drawing involving limited deformation. Appropriate further processing allows a certain degree of cold forming (e.g. bending, expanding) |
| 冷加工（軟） |
最后熱處理之后進(jìn)行小變形量的冷加工， 對(duì)鋼管再加工時(shí)允許有限的冷變形（例如： 彎曲， 擴(kuò)口） |
| Cold finished and stress-relieved |
BKS（+SR） |
Heat treatment is applied following the last cold forming process. Subject to appropriate processing conditions, the increase in the residual stresses involved enables both forming and machining to a certain degree. |
| 冷加工后消除應(yīng)力退火 |
最后冷加工后在Acl點(diǎn)以下進(jìn)行退火， 以消除冷加工應(yīng)力。 |
| Annealed |
GBK（+A） |
The last Cold forming process is followed by annealing in a controlled atmosphere. |
| 退火 |
最后冷加工之后，鋼管在保護(hù)氣體下進(jìn)行完全退火。 |
| Normalized |
NBK（+N） |
The last cold forming process is followed by annealing above the upper transformation point in a controlled atmosphere. |
| 正火 |
最后冷加工之后，鋼管在保護(hù)氣體下進(jìn)行正火。 |